Nozzle: 280 – 300 °C
Printbed: 25˚C – 50˚C
(Do NOT exceed 50 ˚C)
Speed: 60 mm/s
PolyMide™ PA6 CF features Polymaker’s Warp-Free™ technology and Fiber Adhesion™ technology:
Warp-Free™ technology enables the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage. This is achieved by the fine control of microstructure and crystallization behavior of Nylon, which enables the material to fully release the internal stress before solidification.
Fiber Adhesion™ technology improves the layer adhesion of fiber reinforced materials, by optimizing the surface chemistry of the fibers to achieve better dispersion and bonding to the matrix. This results in better strength along the Z-axis and reduced mechanical anisotropy.
Nozzle Temperature: 280˚C – 300˚C
Printing Speed: 60mm/s
Bed Temperature: 25˚C – 50˚C (Do NOT exceed 50 ˚C)
Bed Surface: Glass with glue
Cooling Fan: OFF
Young’s Modulus: 2223 ± 199 Mpa
Tensile Strength: 66.2 ± 0.9 Mpa
Bending Strength: 97.0 ± 1.1 Mpa
Charpy Impact Strength: 9.6 ± 1.4 kJ/m2
Glass Transition Temperature: 67˚C
Vicat Softening Temperature: 180˚C
Melting Temperature: 190˚C
Drying Settings: 80˚C for 12h
Recommended Support Materials: PolyDissolve™ S1
It is highly recommended to use the PolyBox™ when printing with PolyMide™ CoPA and to store it in the resealable bag.
To ensure a good heat resistance of your printed part it is recommended to anneal your PolyMide™ CoPA 3d printed model.
Annealing settings: 70˚C for 2h
Based on 0.4 mm nozzle and Simplify 3D v.3.1. Printing conditions may vary with different printers and nozzle diameters